Our personnel are always inside the spirit of "continuous improvement and excellence", and together with the outstanding excellent goods, favorable price and good after-sales services, we try to gain every customer's trust for Fkm Catalyst, fluoroelastomer fkm, fluorosilicone fvmq, We always regard the technology and customers as the uppermost. We always work hard to create great values for our customers and offer our customers better products & services.

2022 New Style Fkm Kalrez - General Purpose Fluoroelastomer Base Polymer – FUDI Detail:

Viton FKM raw gum is raw material of viton rubber. We supply Chinese best quality of Viton FKM raw gum including Low Mooney, Middle Mooney and high Mooney grades.

FD26 serial FKM raw gum is one kind of copolymer composed of vinylidene fluoride (VDF) and hexafluoropropylene (HFP). It’s a standard type of FKM showing a good overall performance. You may find general properties of the material in below table.

Items	Grades
	FD2601	FD2602	FD2603	FD2604	FD2605
Density (g/cm³)	1.82±0.02	1.82±0.02	1.82±0.02	1.82±0.02	1.82±0.02
Fluorine content (%)	66	66	66	66	66
Mooney Viscosity (ML (1+10)121℃)	25	40~45	60~70	>100	150
Tensile strength after post cure (Mpa) 24h, 230℃	≥11	≥11	≥11	≥13	≥13
Elongation at break after post cure (%)24h, 230℃	≥180	≥150	≥150	≥150	≥150
Compression set (%) 70h, 200℃	≤25

FD24 serial FKM raw gum is one kind of terpolymer composed of vinylidene fluoride (VDF), hexafluoropropylene (HFP) and tetrafluoroethylene (TFE). Terpolymers have a higher fluorine content compare to copolymers (typically between 68 and 69 weight percent fluorine), which
results in better chemical and heat resistance. You may find general properties of the material in below table.

	FD2462	FD2463	FD2465	FD2465L	FD2465H
Fluorine Content	68.5	68.5	68.5	65	69.5
Density (g/cm³)	1.85	1.85	1.85	1.81	1.88
Mooney Viscosity (ML (1+10)121℃)	70±10	40±10	45±15	50±10	40±20
Tensile strength after post cure (Mpa) 24h, 230℃	≥11	≥11	≥11	≥11	≥11
Elongation at break after post cure (%)24h, 230℃	≥180	≥180	≥180	≥180	≥180
Compression set (%) 200℃ 70H compress 20%	≤30%	≤30%	≤30%	≤30%	≤40%
Oil resistance (200℃ 24H) RP-3 oil	≤5%	≤5%	≤5%	≤5%	≤2%
Glass transition temperature (TG)	＞-15℃	＞-15℃	＞-15℃	＞-21℃	＞-13℃
Water content (%)	≤0.15	≤0.15	≤0.15	≤0.15	≤0.15

Package and Storage

Fluoroelastomer are first sealed in PE bag-weights 5kgs per bag, then put into carton box. Net weight per box: 25kgs

Fluoreolastomer should be stored in a cool, dry and ventilated place. Shelf life is 24 months since production date.

Product detail pictures:

Related Product Guide:

Our mission will be to become an innovative supplier of high-tech digital and communication devices by furnishing benefit added structure, world-class manufacturing, and service capabilities for 2022 New Style Fkm Kalrez - General Purpose Fluoroelastomer Base Polymer – FUDI , The product will supply to all over the world, such as: Estonia, Surabaya, Monaco, They are sturdy modeling and promoting effectively all over the world. Never ever disappearing major functions within a quick time, it's a have to for you of fantastic good quality. Guided by the principle of Prudence, Efficiency, Union and Innovation. the corporation. ake an excellent efforts to expand its international trade, raise its organization. rofit and raise its export scale. We are confident that we have been going to have a bright prospect and to be distributed all over the world in the years to come.