Viton FKM raw gum is raw material of viton rubber. We supply Chinese best quality of Viton FKM raw gum including Low Mooney, Middle Mooney and high Mooney grades.
FD26 serial FKM raw gum is one kind of copolymer composed of vinylidene fluoride (VDF) and hexafluoropropylene (HFP). It’s a standard type of FKM showing a good overall performance. You may find general properties of the material in below table.
|
Items |
Grades |
||||
| FD2601 | FD2602 | FD2603 | FD2604 | FD2605 | |
| Density (g/cm3) | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 |
| Fluorine content (%) | 66 | 66 | 66 | 66 | 66 |
| Mooney Viscosity (ML (1+10)121℃) | 25 | 40~45 | 60~70 | >100 | 150 |
| Tensile strength after post cure (Mpa) 24h, 230℃ | ≥11 | ≥11 | ≥11 | ≥13 | ≥13 |
| Elongation at break after post cure (%)24h, 230℃ | ≥180 | ≥150 | ≥150 | ≥150 | ≥150 |
| Compression set (%) 70h, 200℃ |
≤25 |
||||
FD24 serial FKM raw gum is one kind of terpolymer composed of vinylidene fluoride (VDF), hexafluoropropylene (HFP) and tetrafluoroethylene (TFE). Terpolymers have a higher fluorine content compare to copolymers (typically between 68 and 69 weight percent fluorine), which
results in better chemical and heat resistance. You may find general properties of the material in below table.
| FD2462 | FD2463 | FD2465 | FD2465L | FD2465H | |
| Fluorine Content | 68.5 | 68.5 | 68.5 | 65 | 69.5 |
| Density (g/cm3) | 1.85 | 1.85 | 1.85 | 1.81 | 1.88 |
| Mooney Viscosity (ML (1+10)121℃) | 70±10 | 40±10 | 45±15 | 50±10 | 40±20 |
| Tensile strength after post cure (Mpa) 24h, 230℃ | ≥11 | ≥11 | ≥11 | ≥11 | ≥11 |
| Elongation at break after post cure (%)24h, 230℃ | ≥180 | ≥180 | ≥180 | ≥180 | ≥180 |
| Compression set (%) 200℃ 70H compress 20% | ≤30% | ≤30% | ≤30% | ≤30% | ≤40% |
| Oil resistance (200℃ 24H) RP-3 oil | ≤5% | ≤5% | ≤5% | ≤5% | ≤2% |
| Glass transition temperature (TG) | ＞-15℃ | ＞-15℃ | ＞-15℃ | ＞-21℃ | ＞-13℃ |
| Water content (%) | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.15 |
Package and Storage
Fluoroelastomer are first sealed in PE bag-weights 5kgs per bag, then put into carton box. Net weight per box: 25kgs
Fluoreolastomer should be stored in a cool, dry and ventilated place. Shelf life is 24 months since production date.
Product detail pictures:
Related Product Guide:
Our enhancement depends around the sophisticated devices ,exceptional talents and repeatedly strengthened technology forces for Good quality Fkm O Ring Material - General Purpose Fluoroelastomer Base Polymer – FUDI , The product will supply to all over the world, such as: Estonia, Madras, Monaco, So that you can utilize the resource from the expanding info in international trade, we welcome shoppers from everywhere on-line and offline. In spite of the good quality solutions we offer, effective and satisfying consultation service is supplied by our specialist after-sale service team. Product lists and detailed parameters and any other info weil be sent to you timely for your inquiries. So please make contact with us by sending us emails or call us if you have any questions about our corporation. ou may also get our address info from our web page and come to our company to get a field survey of our merchandise. We are confident that we are going to share mutual achievement and create strong co-operation relations with our companions in this marketplace. We're searching forward for your inquiries.
By Ida from Italy - 2017.07.07 13:00
The company can keep up with the changes in this industry market, product updates fast and the price is cheap, this is our second cooperation, it's good.
By Matthew Tobias from Belgium - 2017.10.23 10:29