Hot New Products Fkm Sheet - General Purpose Fluoroelastomer Base Polymer – FUDI

short description:

Stock Sample is Free & Available

Send email to us Whatsapp Email

Product Detail

Product Tags

Feedback (2)

We have a highly efficient team to deal with inquiries from customers. Our goal is "100% customer satisfaction by our product quality, price & our team service" and enjoy a good reputation among clients. With many factories, we can provide a wide range of Viton Extrusion, Fkm Is Viton, Ptfe Powder Lubricant, Any interest, please feel free to contact us. We are looking forward to forming successful business relationships with new clients around the world in the near future.

Hot New Products Fkm Sheet - General Purpose Fluoroelastomer Base Polymer – FUDI Detail:

Viton FKM raw gum is raw material of viton rubber. We supply Chinese best quality of Viton FKM raw gum including Low Mooney, Middle Mooney and high Mooney grades.

FD26 serial FKM raw gum is one kind of copolymer composed of vinylidene fluoride (VDF) and hexafluoropropylene (HFP). It’s a standard type of FKM showing a good overall performance. You may find general properties of the material in below table.

Items	Grades
	FD2601	FD2602	FD2603	FD2604	FD2605
Density (g/cm³)	1.82±0.02	1.82±0.02	1.82±0.02	1.82±0.02	1.82±0.02
Fluorine content (%)	66	66	66	66	66
Mooney Viscosity (ML (1+10)121℃)	25	40~45	60~70	>100	150
Tensile strength after post cure (Mpa) 24h, 230℃	≥11	≥11	≥11	≥13	≥13
Elongation at break after post cure (%)24h, 230℃	≥180	≥150	≥150	≥150	≥150
Compression set (%) 70h, 200℃	≤25

FD24 serial FKM raw gum is one kind of terpolymer composed of vinylidene fluoride (VDF), hexafluoropropylene (HFP) and tetrafluoroethylene (TFE). Terpolymers have a higher fluorine content compare to copolymers (typically between 68 and 69 weight percent fluorine), which
results in better chemical and heat resistance. You may find general properties of the material in below table.

	FD2462	FD2463	FD2465	FD2465L	FD2465H
Fluorine Content	68.5	68.5	68.5	65	69.5
Density (g/cm³)	1.85	1.85	1.85	1.81	1.88
Mooney Viscosity (ML (1+10)121℃)	70±10	40±10	45±15	50±10	40±20
Tensile strength after post cure (Mpa) 24h, 230℃	≥11	≥11	≥11	≥11	≥11
Elongation at break after post cure (%)24h, 230℃	≥180	≥180	≥180	≥180	≥180
Compression set (%) 200℃ 70H compress 20%	≤30%	≤30%	≤30%	≤30%	≤40%
Oil resistance (200℃ 24H) RP-3 oil	≤5%	≤5%	≤5%	≤5%	≤2%
Glass transition temperature (TG)	＞-15℃	＞-15℃	＞-15℃	＞-21℃	＞-13℃
Water content (%)	≤0.15	≤0.15	≤0.15	≤0.15	≤0.15

Package and Storage

Fluoroelastomer are first sealed in PE bag-weights 5kgs per bag, then put into carton box. Net weight per box: 25kgs

Fluoreolastomer should be stored in a cool, dry and ventilated place. Shelf life is 24 months since production date.

Product detail pictures:

Related Product Guide:

Persisting in "High high quality, Prompt Delivery, Aggressive Price", we've established long-term cooperation with clients from the two overseas and domestically and get new and old clients' superior comments for Hot New Products Fkm Sheet - General Purpose Fluoroelastomer Base Polymer – FUDI , The product will supply to all over the world, such as: Albania, Sierra Leone, Botswana, We welcome an opportunity to do business with you and hope to have pleasure in attaching further details of our products. Excellent quality, competitive price, punctual delivery and dependable service can be guaranteed. For further inquires please do not hesitate to contact us.

perfluoroelastomer ffkm

Viton And Fkm

This supplier stick to the principle of "Quality first, Honesty as base", it is absolutely to be trust.