Viton FKM raw gum is raw material of viton rubber. We supply Chinese best quality of Viton FKM raw gum including Low Mooney, Middle Mooney and high Mooney grades.
FD26 serial FKM raw gum is one kind of copolymer composed of vinylidene fluoride (VDF) and hexafluoropropylene (HFP). It’s a standard type of FKM showing a good overall performance. You may find general properties of the material in below table.
|
Items |
Grades |
||||
| FD2601 | FD2602 | FD2603 | FD2604 | FD2605 | |
| Density (g/cm3) | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 |
| Fluorine content (%) | 66 | 66 | 66 | 66 | 66 |
| Mooney Viscosity (ML (1+10)121℃) | 25 | 40~45 | 60~70 | >100 | 150 |
| Tensile strength after post cure (Mpa) 24h, 230℃ | ≥11 | ≥11 | ≥11 | ≥13 | ≥13 |
| Elongation at break after post cure (%)24h, 230℃ | ≥180 | ≥150 | ≥150 | ≥150 | ≥150 |
| Compression set (%) 70h, 200℃ |
≤25 |
||||
FD24 serial FKM raw gum is one kind of terpolymer composed of vinylidene fluoride (VDF), hexafluoropropylene (HFP) and tetrafluoroethylene (TFE). Terpolymers have a higher fluorine content compare to copolymers (typically between 68 and 69 weight percent fluorine), which
results in better chemical and heat resistance. You may find general properties of the material in below table.
| FD2462 | FD2463 | FD2465 | FD2465L | FD2465H | |
| Fluorine Content | 68.5 | 68.5 | 68.5 | 65 | 69.5 |
| Density (g/cm3) | 1.85 | 1.85 | 1.85 | 1.81 | 1.88 |
| Mooney Viscosity (ML (1+10)121℃) | 70±10 | 40±10 | 45±15 | 50±10 | 40±20 |
| Tensile strength after post cure (Mpa) 24h, 230℃ | ≥11 | ≥11 | ≥11 | ≥11 | ≥11 |
| Elongation at break after post cure (%)24h, 230℃ | ≥180 | ≥180 | ≥180 | ≥180 | ≥180 |
| Compression set (%) 200℃ 70H compress 20% | ≤30% | ≤30% | ≤30% | ≤30% | ≤40% |
| Oil resistance (200℃ 24H) RP-3 oil | ≤5% | ≤5% | ≤5% | ≤5% | ≤2% |
| Glass transition temperature (TG) | ＞-15℃ | ＞-15℃ | ＞-15℃ | ＞-21℃ | ＞-13℃ |
| Water content (%) | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.15 |
Package and Storage
Fluoroelastomer are first sealed in PE bag-weights 5kgs per bag, then put into carton box. Net weight per box: 25kgs
Fluoreolastomer should be stored in a cool, dry and ventilated place. Shelf life is 24 months since production date.
Product detail pictures:
Related Product Guide:
We have our own sales team, design team, technical team, QC team and package team. We have strict quality control procedures for each process. Also, all of our workers are experienced in printing field for OEM/ODM Supplier Bisphenol Cured Fkm - General Purpose Fluoroelastomer Base Polymer – FUDI , The product will supply to all over the world, such as: Anguilla, Qatar, Maldives, With the technology as the core, develop and produce high-quality merchandise according to the diverse needs of the market. With this concept,the company will continue to develop merchandise with high added values and continuously improve items,and will present many customers with the best goods and services!
By Yannick Vergoz from Angola - 2018.04.25 16:46
It is not easy to find such a professional and responsible provider in today's time. Hope that we can maintain long-term cooperation.
By Emma from Nepal - 2018.12.10 19:03