Well-designed Kalrez Ffkm - General Purpose Fluoroelastomer Base Polymer – FUDI
Stock Sample is Free & Available
Well-designed Kalrez Ffkm - General Purpose Fluoroelastomer Base Polymer – FUDI Detail:
Viton FKM raw gum is raw material of viton rubber. We supply Chinese best quality of Viton FKM raw gum including Low Mooney, Middle Mooney and high Mooney grades.
FD26 serial FKM raw gum is one kind of copolymer composed of vinylidene fluoride (VDF) and hexafluoropropylene (HFP). It’s a standard type of FKM showing a good overall performance. You may find general properties of the material in below table.
|
Items |
Grades |
||||
| FD2601 | FD2602 | FD2603 | FD2604 | FD2605 | |
| Density (g/cm3) | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 | 1.82±0.02 |
| Fluorine content (%) | 66 | 66 | 66 | 66 | 66 |
| Mooney Viscosity (ML (1+10)121℃) | 25 | 40~45 | 60~70 | >100 | 150 |
| Tensile strength after post cure (Mpa) 24h, 230℃ | ≥11 | ≥11 | ≥11 | ≥13 | ≥13 |
| Elongation at break after post cure (%)24h, 230℃ | ≥180 | ≥150 | ≥150 | ≥150 | ≥150 |
| Compression set (%) 70h, 200℃ |
≤25 |
||||
FD24 serial FKM raw gum is one kind of terpolymer composed of vinylidene fluoride (VDF), hexafluoropropylene (HFP) and tetrafluoroethylene (TFE). Terpolymers have a higher fluorine content compare to copolymers (typically between 68 and 69 weight percent fluorine), which
results in better chemical and heat resistance. You may find general properties of the material in below table.
| FD2462 | FD2463 | FD2465 | FD2465L | FD2465H | |
| Fluorine Content | 68.5 | 68.5 | 68.5 | 65 | 69.5 |
| Density (g/cm3) | 1.85 | 1.85 | 1.85 | 1.81 | 1.88 |
| Mooney Viscosity (ML (1+10)121℃) | 70±10 | 40±10 | 45±15 | 50±10 | 40±20 |
| Tensile strength after post cure (Mpa) 24h, 230℃ | ≥11 | ≥11 | ≥11 | ≥11 | ≥11 |
| Elongation at break after post cure (%)24h, 230℃ | ≥180 | ≥180 | ≥180 | ≥180 | ≥180 |
| Compression set (%) 200℃ 70H compress 20% | ≤30% | ≤30% | ≤30% | ≤30% | ≤40% |
| Oil resistance (200℃ 24H) RP-3 oil | ≤5% | ≤5% | ≤5% | ≤5% | ≤2% |
| Glass transition temperature (TG) | ＞-15℃ | ＞-15℃ | ＞-15℃ | ＞-21℃ | ＞-13℃ |
| Water content (%) | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.15 | ≤0.15 |
Package and Storage
Fluoroelastomer are first sealed in PE bag-weights 5kgs per bag, then put into carton box. Net weight per box: 25kgs
Fluoreolastomer should be stored in a cool, dry and ventilated place. Shelf life is 24 months since production date.
Product detail pictures:
Related Product Guide:
We strive for excellence, service the customers", hopes to become the best cooperation team and dominator enterprise for personnel, suppliers and customers, realizes value share and continuous promotion for Well-designed Kalrez Ffkm - General Purpose Fluoroelastomer Base Polymer – FUDI , The product will supply to all over the world, such as: Ecuador, Las Vegas, Indonesia, By integrating manufacturing with foreign trade sectors, we can provide total customer solutions by guaranteeing the delivery of right products to the right place at the right time, which is supported by our abundant experiences, powerful production capability, consistent quality, diversified products and the control of the industry trend as well as our maturity before and after sales services. We'd like to share our ideas with you and welcome your comments and questions.
By Ivan from Bangladesh - 2018.03.03 13:09
The supplier cooperation attitude is very good, encountered various problems, always willing to cooperate with us, to us as the real God.
By Diana from Dubai - 2017.03.08 14:45